Incidence of the oxyacetilenic flame on the welding of a nodular iron with bronze filled metal
Keywords:
microstructure, dendrites, nodular iron, oxyacetylene.Abstract
The incidence of the oxyacetylene flame in the welding of a nodular iron with bronze filler metal was determined. The process was carried out with a neutral flame and with a RBCuZn-C type bronze rod with a diameter of 2.4 mm. In the weld bead, a molten zone is obtained with the presence of ferrite, dendrites of primary α phase and Widmanstätten structure, as well as pearlite between the edges of the grains. The interface preceded by the formation of martensite and degenerate graphite nodules and in the heat affected zone graphite nodules in a ferrite-pearlite matrix. The hardness in the different zones, from the base material, increases from 170 HV to 234 HV, being higher in the molten zone.Downloads
References
ASTM A536-84. 2014. Standard Specification for Ductile Iron Castings. ASTM International, West Conshohocken, PA.
AMERICAN WELDING SOCIETY AWS-AWS D11.2-1989-R2006 Guide for Welding Iron Castings-AWS. Consulta: 15 feb 2019. Disponible en: https://kupdf.net/download/american-welding-society-aws-aws-d11-2-1989-r2006-guide-for-welding-iron-castings-aws_59f6c103e2b6f530247f12f6_pdf#
CEMBRERO, J. Y PASCUAL, M. 1999. Soldabilidad de las fundiciones de grafito esferoidal. Rev. Metal 35(2): 392-401.
CEREDO-HERNÁNDEZ, E. Y OLGUIN-MONTOYA, J. 2016. Recuperación de piezas de hierro colado por soldadura. Tesis de la Escuela Superior de Ingeniería Mecánica y Eléctrica. Unidad Azcapotzalco. Ciudad de México.
FERNÁNDEZ-COLUMBIÉ, T.; RODRÍGUEZ-GONZÁLEZ, I.; CORREA-SUÁREZ, R. Y ALCÁNTARA-BORGES, D. 2014. Junta de soldadura disímil de la aleación HK-40 y del hierro fundido 24. Ingeniería Mecánica 17(2): 98-107.
FERRER, C.; SALAS, F.; MAITA, P. A.; OROZCO, J. Y PASCUAL, M. 2007. Resistencia a la fractura de la soldadura de fundición dúctil realizada con varillas de fundición laminar y con electrodos de Fe-Cr-Ni y de Ni, con y sin precalentamiento. Anales de la Mecánica de Fractura 2(1): 533-536.
KUK, J.; JANG, K.; LEE, D. Y KIM, I. 2004. Effects of temperature and shielding gas mixture on fatigue life of 5083 aluminum alloy. Journal of Materials Processing Technology (155–156): 1408-1414.
LUDDEY, J.; MARULANDA, A. Y MESA, D. 2007. Recuperación y soldabilidad de fundición de hierro. Scientia Et Technica XIII(037): 237-242.
MORENO-RODRÍGUEZ, R. Y PASCUAL-GUILLAMÓN, M. 2016. Soldadura de fundición dúctil con fundición gris y aporte de varilla de níquel al 98% procedimiento TIG. Proyecto final de grado. Valencia. 50 p.
POURANVARI, M. 2010. On the weldability of grey cast iron using nickel-based filler metal. Dezful 31(3): 32-54.
RAMOS, F.; POZO, J.; DÍAZ, E. Y VELÁSQUEZ, E. 2005. Reparación por soldadura de tapas agrietadas, de hierro fundido. Revista Facultad de Ingeniería Universidad de Antioquia, Colombia 34: 35-41.
VIADA-ESTÉVEZ, A. Y FERNÁNDEZ-COLUMBIÉ, T. 2020. Comportamiento de la microestructura de uniones de hierro fundido con diferentes materiales de aporte. Minería y Geología 36(1): 92-105.
Published
How to Cite
Issue
Section
Esta obra está bajo una Licencia Creative Commons Reconocimiento-NoComercial 4.0 Internacional
La Revista Ciencia & Futuro es una revista de acceso abierto, todo el contenido está disponible gratuitamente sin cargo para el usuario o su institución. Los usuarios pueden leer, descargar, copiar, distribuir, imprimir, buscar o vincular los textos completos de los artículos, o utilizarlos para cualquier otro fin lícito, sin pedir permiso previo al editor o al autor. Todo lo anterior, de acuerdo con la definición de BOAI de acceso abierto.
Los autores que publican en esta revista están de acuerdo con los siguientes términos: Licencia Creative Commons Atribución-NoComercial permite que el beneficiario de la licencia tenga el derecho de copiar, distribuir, exhibir y representar la obra y hacer obras derivadas para fines no comerciales siempre y cuando reconozca y cite la obra de la forma especificada por el autor o el licenciante. Los autores pueden establecer por separado acuerdos adicionales para la distribución no exclusiva de la versión de la obra publicada en la revista (por ejemplo, situarlo en un repositorio institucional o publicarlo en un libro), con un reconocimiento de su publicación inicial en esta revista. Se permite y se anima a los autores a difundir sus trabajos electrónicamente (por ejemplo, en repositorios institucionales o en su propio sitio web) antes y durante el proceso de envío, ya que puede dar lugar a intercambios productivos, así como a una citación más temprana y mayor de los trabajos publicados (Véase The Effect of Open Access) (en inglés). Lo anterior debe realizarse siempre sobre el artículo ya publicado por Ciencia & Futuro.
Los autores mantienen el control sobre la integridad de sus trabajos y el derecho a ser adecuadamente reconocidos y citados.
A los editores se les otorgan derechos no exclusivos para publicar y distribuir.