Steel structure API 5L GR. 65 soldier with electric arc and coated electrode
Keywords:
structure, API 5L, pipe, cord zones, encapsulated.Abstract
The structures generated in the area of the strand of an API 5L Gr. 65 pipe steel of 100 mm in diameter and 7 mm in thickness, welded with an E 7018 electrode of 4 mm in diameter, were determined. For the deposit of the cords, the preparation was carried out at the top with a 60o bevel, samples were cut for hardness tests, chemical composition and observation with light microscopy, all of them were encapsulated with ROYAPOX-5050 resin. In the first cord the structures obtained are made of ferrite + pearlite with fine grain in the molten zone and the one affected by heat, not being the case at the interface where the grains are coarser, in the second the same structures are obtained, but from smaller grains due to multipass welding. It is determined that the hardness in the first cord is 238 HV, which decreases in the 2nd to 217 HV, this property being affected by the effect of heat.Downloads
References
ABEDI, S. 2017. Failure investigation of a defective weldment of an oil product transmission pipeline. J. Fail. Anal. Prev. 17(1): 30-37.
ALMAGUER‐ZALDIVAR, P. & ESTRADA‐CINGUALBRES, R. 2015. Evaluación del comportamiento a fatiga de una unión soldada a tope de acero AISI 1015. Ingeniería Mecánica 18 (1): 31-41.
API 1104 EDICIÓN 2010. Welding of Pipelines and Related Facilities, Pipeline Segment, American Petroleum Institute, Reafirmed April (2010). API Publishing Services, Washington, D.C.
CHILQUE, A.; JARDIM, M.; GONÇALVES, P. & TAVARES, S. 2014. Determinação da resistência ao impacto da região de grão grosseiro da ZTA do aço API5L X80 soldado em condições de alta energia. Congr. Nac. Soldag.
DA COSTA, A.; SILVA, L. & MEI, P. 2010. Aços e ligas especiais. 3rd ed. Blucher, São Paulo.
SANTOS, I. M. D. C. 2013. Elaboração de um diagrama TAC para um aço de alta tenacidade API X-70. Doctoral dissertation. Universidade Nova de Lisboa.
GONZÁLEZ-CABRERA, O.; GÓMEZ-PÉREZ, C.; PERDOMO-GONZÁLEZ, L. & VÁZQUEZ-BADILLO, E. 2017. Comportamiento de la resistencia al desgaste entre depósitos obtenidos con electrodos simple y doblemente recubiertos. Soldagem & Inspeção 22(1): 87-98.
JUNIOR, J.; ROCHA, D. & BRANDI, S. 2013. Uma breve revisão histórica do desenvolvimento da soldagem dos aços API para tubulações. Soldagem e Inspeção, São Paulo 25(12): 176-195.
LAMBERT, A.; DRILLET, J.; GOURGUES, A.; STUREL, T. & PINEAU, H. 2004. Austenite to bainite phase transformations in the heat-affected zone of a high strength low alloy steel. Acta Materialia 52(6): 2337-2348.
LI, C.; WANG, Y.; HAN, T.; HAN, B. & LI, L. 2010. Microstructure and toughness of coarse grain heat-affected zone of domestic X70 pipeline steel during in-service welding. J. Mater. Sci. 46(3): 727-733.
MELGAREJO, M.; RAMÍREZ, C. & APERADOR, W. 2013. Determinación de las causas de falla en la ZAC de un Acero ASTM A36 soldado por proceso SMAW. Revista Inge CuC 9(2): 75-82.
MODENESI, P.; MARQUES, P. & SANTOS, D. 2012. Introdução à Metalurgia da Soldagem. UFMG, Belo Horizonte, p. 209.
ORDÓÑEZ, R. 2004. Soldagem e caracterização das propriedades mecânicas de dutos de aço API 5L-X80 com diferentes arames tubulares. UNICAMP.
PICHARDO, B.; LÓPEZ, V.; HERNÁNDEZ, R. & SALAZAR, M. 2019. Microestructura y propiedades mecánicas de una junta soldada de placas bicapa API X60/316L. Ava Cient. VII(2): 135-145.
REYES-CARCASÉS, D.; FERNÁNDEZ-COLUMBIÉ, T.; ALCÁNTARA-BORGES, D. & RODRÍGUEZ-GONZÁLEZ, I. 2018. Soldadura con los electrodos revestidos E 6010 y E 7018 en acero AISI 1025. Minería y Geología 34(1): 108-121.
Published
How to Cite
Issue
Section
Copyright (c) 2021 António Quizila-Ricardo, Tomás Fernández-Columbié
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.
Esta obra está bajo una Licencia Creative Commons Reconocimiento-NoComercial 4.0 Internacional
La Revista Ciencia & Futuro es una revista de acceso abierto, todo el contenido está disponible gratuitamente sin cargo para el usuario o su institución. Los usuarios pueden leer, descargar, copiar, distribuir, imprimir, buscar o vincular los textos completos de los artículos, o utilizarlos para cualquier otro fin lícito, sin pedir permiso previo al editor o al autor. Todo lo anterior, de acuerdo con la definición de BOAI de acceso abierto.
Los autores que publican en esta revista están de acuerdo con los siguientes términos: Licencia Creative Commons Atribución-NoComercial permite que el beneficiario de la licencia tenga el derecho de copiar, distribuir, exhibir y representar la obra y hacer obras derivadas para fines no comerciales siempre y cuando reconozca y cite la obra de la forma especificada por el autor o el licenciante. Los autores pueden establecer por separado acuerdos adicionales para la distribución no exclusiva de la versión de la obra publicada en la revista (por ejemplo, situarlo en un repositorio institucional o publicarlo en un libro), con un reconocimiento de su publicación inicial en esta revista. Se permite y se anima a los autores a difundir sus trabajos electrónicamente (por ejemplo, en repositorios institucionales o en su propio sitio web) antes y durante el proceso de envío, ya que puede dar lugar a intercambios productivos, así como a una citación más temprana y mayor de los trabajos publicados (Véase The Effect of Open Access) (en inglés). Lo anterior debe realizarse siempre sobre el artículo ya publicado por Ciencia & Futuro.
Los autores mantienen el control sobre la integridad de sus trabajos y el derecho a ser adecuadamente reconocidos y citados.
A los editores se les otorgan derechos no exclusivos para publicar y distribuir.