Distribution of temperatures in a gray iron for the incidence of the thermal cycle of welding
Keywords:
isotherm, thermal cycle of welding, gray iron, temperature.Abstract
The influence of the thermal welding cycle of the gray cast iron was established, as well as the behavior of the isotherms during the heating and cooling of the material. For the study, a bevel joint was considered in simple V at 60o, in a thickness of 12 millimeters. The parameters analyzed were the current intensity, the arc voltage, the welding speed, as well as the linear energy of the process and the incoming energy. To establish the isotherms, temperatures of 900, 800, 600 and 200 oC, were taken at different distances from the welding arc. It was determined that during the thermal cycle, the distribution of temperature along the seam in the branch of heating and cooling, in the first, the curves is more abrupt, that is, have higher slope than in the branches of cooling.Downloads
References
AGUILAR, W. & BOERI, R. 2000. Comportamiento a la segregación de los elementos de aleación usados en fundiciones esferoidales de fabricación. Jornadas SAM – IV Coloquio Latinoamericano de Fractura y Fatiga. Agosto, Neuquén, Argentina, p. 123-130.
BARSOUM, Z. & LUNDBÄCK, A. 2009. Simplified FE welding simulation of fillet welds-3D effects on the formation residual stresses. Engineering Failure Analysis 16(16): 22-31.
BOTT, I.; SOUZA, L.; TEIXEIRA, J. & RIOS, P. 2005. High-strength steel development for pipelines: a Brazilian perspective. Metallurgical and Materials Transaction 36(2): 443-454.
FERNÁNDEZ-COLUMBIÉ, T.; RODRÍGUEZ-GONZÁLEZ, I.; CORREA-SUÁREZ, R. & ALCÁNTARA-BORGES, D. 2014. Junta de soldadura disímil de la aleación HK-40 y del hierro fundido 24. Ingeniería Mecánica 17(2): 98-107.
FERRER, C.; SALAS, F.; MAITA, P.; OROZCO, J. & PASCUAL, M. 2007. Resistencia a la fractura de la soldadura de fundición dúctil realizada con varillas de fundición laminar y con electrodos de Fe-Cr-Ni y de Ni, con y sin precalentamiento. Anales de la Mecánica de Fractura 2(1): 533-536.
GUIRAO, J.; RODRÍGUEZ, E.; BAYÓN, A.; BOUYER, F.;
PISTONO, J. & JONES, L. 2010. Determination through the distortions analysis of the best welding sequence in longitudinal welds VATS electron beam welding FE simulation. Fusion Engineering and Design 85(78): 766-779.
JU-SEOK, K. 2008. Characterization of bainitic microstructures in low carbon HSLA steels. International Journal of Moder Phisics B 22(31): 5965-5970.
MARULANDA, A.; LUDDEY, J. & MESA, D. 2007. Recuperación y soldabilidad de fundición de hierro. Scientia Et Technica 13(37): 237-242.
MELÉNDEZ-TORT, T. 2016. Aplicación del ciclo térmico de soldadura en pieza agrietada de hierro fundido. Tesis de grado. Instituto Superior Minero Metalúrgico de Moa.
PAKANDAM, F.; VARVANI, F. & ARAHANI, A. 2011. Fatigue damage assessment of various welded joints under uniaxial loading based on energy methods. International Journal of Fatigue 33(4): 519–28.
POURANVARI, M. 2010. On the weldability of grey cast iron using nickel based filler metal. Materials & Design 31(7): 3253-3258.
RAMOS, F.; POZO, J.; DÍAZ, E. & VELÁSQUEZ, E. 2005. Reparación por soldadura de tapas, agrietadas, de hierro fundido. Revista Facultad de Ingeniería, Universidad de Antioquia, Colombia 34: 35-41.
ZINN, W. & SCHOLTES, B. 2002. Handbook of residual stresses and deformation of steel. G. Totten, M. Howes and T. Inoue (Ed). ASM International, U.S.A., p. 391-396.
Published
How to Cite
Issue
Section
Esta obra está bajo una Licencia Creative Commons Reconocimiento-NoComercial 4.0 Internacional
La Revista Ciencia & Futuro es una revista de acceso abierto, todo el contenido está disponible gratuitamente sin cargo para el usuario o su institución. Los usuarios pueden leer, descargar, copiar, distribuir, imprimir, buscar o vincular los textos completos de los artículos, o utilizarlos para cualquier otro fin lícito, sin pedir permiso previo al editor o al autor. Todo lo anterior, de acuerdo con la definición de BOAI de acceso abierto.
Los autores que publican en esta revista están de acuerdo con los siguientes términos: Licencia Creative Commons Atribución-NoComercial permite que el beneficiario de la licencia tenga el derecho de copiar, distribuir, exhibir y representar la obra y hacer obras derivadas para fines no comerciales siempre y cuando reconozca y cite la obra de la forma especificada por el autor o el licenciante. Los autores pueden establecer por separado acuerdos adicionales para la distribución no exclusiva de la versión de la obra publicada en la revista (por ejemplo, situarlo en un repositorio institucional o publicarlo en un libro), con un reconocimiento de su publicación inicial en esta revista. Se permite y se anima a los autores a difundir sus trabajos electrónicamente (por ejemplo, en repositorios institucionales o en su propio sitio web) antes y durante el proceso de envío, ya que puede dar lugar a intercambios productivos, así como a una citación más temprana y mayor de los trabajos publicados (Véase The Effect of Open Access) (en inglés). Lo anterior debe realizarse siempre sobre el artículo ya publicado por Ciencia & Futuro.
Los autores mantienen el control sobre la integridad de sus trabajos y el derecho a ser adecuadamente reconocidos y citados.
A los editores se les otorgan derechos no exclusivos para publicar y distribuir.