Stresses induced by the thermal welding cycle in an API 5l grade x 65 steel
Keywords:
alloy, metal constructions, welded jointAbstract
The behavior of the stresses that arise during the welding process of an API 5L Gr. 65 steel pipe was analyzed due to the effect of temperature and heat flow. The simulation was carried out considering the deposit of the bead in a diameter of 100 mm with a 4 mm E 7018 electrode, as conditions. It was determined that the stresses generated in the thermal welding cycle are distributed with values from 443.55 N/mm2, in the molten zone, at the interface it is 394.31 N/mm2 and in the zone affected by the heat of 345.06 N/mm2, which influence the fatigue resistance of the joint. The maximum temperature value originates in the center of the weld bead with 3,500 oC and as it moves away from it it decreases to 507.41 oC, which is associated with the heat transfer process by radiation and conduction and that the localized heating of the welding process causes thermal deformations of an elastic and plastic nature.Downloads
References
ABHISHEK, B., ANILKUMAR, G. & MADHUSUDHAN, T. (2015). Experimental and finite element analysis of therm allyinduced residual stresses for stainless steel 303 grade using GMAW process. International Research Journal of Engineering and Technology, 2(2), 160-6.
BAO, R. & ZHANG, X. (2010). An inverse method for evaluating weld residual stresses via fatigue crack growth test data. Engineering Fracture Mechanics, 77(7), 3143-3156.
BURGAN, B., BADDOO, N. & GILSENAN, K. (2000). Structural design of stainless-steel members comparison between Eurocode 3, Part. 1.4 And test results. Journal of Constructional Steel Research, 54(32), 51-73. http://www.sciencedirect.com/science/article/abs/pii/s0143974X9.
CHILQUE, A., JARDIM, M., GONÇALVES, P. & TAVARES, S. (2014). Determinação da resistência ao impacto da região de grão grosseiro da ZTA do aço API5L X80 soldado em condições de alta energia. Congr. Nac. Soldag.
FOSCA, C. (2007). Introducción a la Metalurgia de la Soldadura. Séptima Edición. Pontificia Universidad Católica del Perú.
GIANETTO, J., FAZELI, F. & CHEN, Y. (2014). Microstructure and Toughness of Simulated Grain Coarsened Heat Affected Zones in X80 Pipe Steels, 10th International Pipeline Conference, Calgary, Canada.
GONCALVES, C. (2006). Estimation of heat source and thermal efficiency in GTAW process by using inverse techniques. Journal of Materials Processing Technology, 172(17), 42-51. https://doi.org/10.10.16/j.jmatprotec.2005.08.010.
KANVINDE, A., FELL, B., GOMEZ, I. & ROBERTS, M. (2008). Predicting fracture in structural fillet welds using traditional and micromechanical fracture models. Engineering Structures, 30(11), 3325-3335. https://doi.org/10.10.16/j.engstruct.2008.05.014.
KARUNAKARAN, N. & BALASUBRAMANIAN, V. (2011). Multipurpose three-dimensional finite element procedure for therm analysis in pulsed current gas tungsten arc welding of AZ 31B magnesium alloy sheets. World Academy of Science, Engineering and Technology, 5(3), 29-36. https://doi.org/10.5281/zenodo.1328306.
LAMBERT, A, GOURGUES, A., & PINEAU, H. (2004). Austenite to bainite phase transformations in the heat-affected zone of a high strength low alloy steel. Acta Materialia, 52(6), 2337-2348. https://doi.org/10.1016/j.actamat.2004.01.025.
MOHTADI-BONAB, M., SZPUNAR, J. & RAZAVI-TOUSI, S. A (2013). Comparative study of hydrogen induced cracking behavior in API 5L X60 and X70 pipeline steels. Análisis de fallas de ingeniería, 33(7), 163-175. https://doi.org/10.1016/j.engfailanal.2013.04.028.
NARAYANAREDDY, V., CHANDRASEKHAR, N. & VASUDEVAN, M. (2015). Numerical simulation and artificial neural network modeling for predicting welding induced distortion in butt welded 304L stainless steel plates. Metallurgical and Materials Transactions B, 1(1), 702-703. https://doi.org/10.1007/s11663015-0468-x.
NAYAR, A. (1997). The Metal Databook. McGraw-Hill.
OSMAR, G. (2016). Determinación de deformaciones y tensiones residuales en tuberías unidas por soldadura utilizando simulación numérica para su aplicación en gasoductos. Lima, Perú: Pontificia Universidad Católica del Perú.
PENG-HSIANG, C. & TSO-LIANG, T. (2008). Numerical and experimental investigations on the fatigue evaluation of butt-welded joints. Metals and Materials International, 14(3), 361-72. https://doi.org/10.3365/met.mat.2008.06.361.
POZO, J., QUINTERO, P. & CRUZ, C. (2011). Análisis térmico de soldadura GTAW sobre placa de acero AISI 316L empleando el método de elementos finitos. Soldagem Inspesao, 16(3), 256-64. https://doi.org/10.1590/S0104-92242011000300007.
SHIGLEY, J. & MISCHKE, C. (1998). Diseño en Ingeniería Mecánica. 4a ed. México, McGraw Hill.
SUSMEL, L. & ASKES, H. (2012). Método modificado de la curva de Wholer y evaluación de la fatiga multiaxial de uniones soldadas delgadas. Revista Internacional de Fatiga, 43, 30-42.
TRAIDIA, A. & ROGER, F. (2011). Numerical and experimental study of arc and weld pool behaviour for pulsed current GTA welding. International Journal of Heat and Mass Transfer, 54(9-10), 2163-2179. https://doi.org/10.1016/j.ijheatmasstransfer.2010.12.005.
WAHEED, R., SHAKOOR, A., AZAM, K., KHAN, A. & SHAH, F. (2015). Welding distortion control in thin metal plates by altering heat input through weld parameters. Technical Journal, University of Engineering and Technology, 20(II), 171-177.
Published
How to Cite
Issue
Section
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.
Esta obra está bajo una Licencia Creative Commons Reconocimiento-NoComercial 4.0 Internacional
La Revista Ciencia & Futuro es una revista de acceso abierto, todo el contenido está disponible gratuitamente sin cargo para el usuario o su institución. Los usuarios pueden leer, descargar, copiar, distribuir, imprimir, buscar o vincular los textos completos de los artículos, o utilizarlos para cualquier otro fin lícito, sin pedir permiso previo al editor o al autor. Todo lo anterior, de acuerdo con la definición de BOAI de acceso abierto.
Los autores que publican en esta revista están de acuerdo con los siguientes términos: Licencia Creative Commons Atribución-NoComercial permite que el beneficiario de la licencia tenga el derecho de copiar, distribuir, exhibir y representar la obra y hacer obras derivadas para fines no comerciales siempre y cuando reconozca y cite la obra de la forma especificada por el autor o el licenciante. Los autores pueden establecer por separado acuerdos adicionales para la distribución no exclusiva de la versión de la obra publicada en la revista (por ejemplo, situarlo en un repositorio institucional o publicarlo en un libro), con un reconocimiento de su publicación inicial en esta revista. Se permite y se anima a los autores a difundir sus trabajos electrónicamente (por ejemplo, en repositorios institucionales o en su propio sitio web) antes y durante el proceso de envío, ya que puede dar lugar a intercambios productivos, así como a una citación más temprana y mayor de los trabajos publicados (Véase The Effect of Open Access) (en inglés). Lo anterior debe realizarse siempre sobre el artículo ya publicado por Ciencia & Futuro.
Los autores mantienen el control sobre la integridad de sus trabajos y el derecho a ser adecuadamente reconocidos y citados.
A los editores se les otorgan derechos no exclusivos para publicar y distribuir.