Effect of the torsion in samples of i steel aisi 1045 deformed for rolling
Keywords:
deformation in cold, torsion, microstructure, acrimony, simple roller.Abstract
The objective of the work is to establish the behaviour microestructural and that of the stress in the steel AISI 1045 after having been subjected to process of deformation in cold with the employment of simple roller and then torsion. Were selected nine samples, which were deformed with parameters of: it forces of 500, 1 500 and 2 500 N; advance of 0,075; 0,125 and 0,25, as well as with numbers of revolutions of 27, 54 and 110 r/min. after the process it was determined that a decrease exists in the size grain from the number 5 up to the 10 when applying the maximum parameters of deformation, in a same way, an increment of the stress exists from 515,8 N/mm2 for force of 500 N, up to 651,7 N/mm2for the deformed samples with force of 2 500 N with the increment of the hardness up to 448 HV. It is determined that the variations that happen in the steel AISI 1045 after the combined processes, are for effect of the acrimony.Downloads
References
ÁLVAREZ, E.; LANCESTREMERE, J., MAREGLIA, J. & BARR, J. 2004. Fundamentos de la trafilación. Tecnología Mecánica II. Universidad de Buenos Aires.
EL-KHABEERY, M. 2003. Influence of orthogonal burnishing parameters on surface characteristics for various materials. Journal of Materials Processing Technology 132(1-3): 82-89.
FERNÁNDEZ, T.; FERNÁNDEZ, E.; RODRÍGUEZ, I. & ALCÁNTARA, D. 2008. Procedimiento para endurecer el acero 45 mediante la deformación plástica con rodillo simple. Ingeniería e Investigación 28(1): 15-21.
F
ERNÁNDEZ, T.; RODRÍGUEZ, I. & ALCÁNTARA, D. 2009. Tensión–Deformación durante la deformación plástica superficial con rodillo. Revista de Ingeniería Mecánica 12(3): 13-22.
FERNÁNDEZ, T.; RODRÍGUEZ, I. & ALCÁNTARA, D. 2010. Variación microestructural del acero AISI 1045 endurecido por rodadura. Minería y Geología 26(3): 65-74.
FERNÁNDEZ, T.; FERNÁNDEZ, E.; RODRÍGUEZ, I. & ALCÁNTARA, D. 2011. Evaluación del coeficiente de endurecimiento del acero AISI 1045 deformado por rodillo. Revista Nexo 24(2): 16-26.
FERNÁNDEZ, T.; FERNÁNDEZ, E.; RODRÍGUEZ, I.; ALCÁNTARA, D. & CASTILLO, R. 2013. Comportamiento microestructural del acero AISI 1045 endurecido en frío y traccionado. Revista de la Facultad de Ingeniería U.C.V. 28(3): 49-54.
FERNÁNDEZ, T.; RODRÍGUEZ, I.; ALCÁNTARA, D. & GAINZA, N. 2017. Movimiento por cicloide en la deformación en frío del acero AISI 1045 empleando rodillo. Minería y Geología 33(1): 76-93.
LUBRINER, J. 1986. Plasticity theory. Dover publications, Inc., New York, Charter 2, p. 77-86.
MORENO, G.; CAPO, J.; FERNÁNDEZ, T. & AYARDE, D. 2014. La emisión magnética Barkhausen en el acero AISI 1045 deformado plásticamente con rodillo. Revista Cubana de Física 31(1): 19-21.
PERO, J. 2000. Metalurgia física: Estructura y propiedades. En: Ciencia e ingeniería de materiales. 3ra Ed. S.L. CIE Inversiones Editoriales DOSSAT-2000, España, p. 393-502.
Published
How to Cite
Issue
Section
Esta obra está bajo una Licencia Creative Commons Reconocimiento-NoComercial 4.0 Internacional
La Revista Ciencia & Futuro es una revista de acceso abierto, todo el contenido está disponible gratuitamente sin cargo para el usuario o su institución. Los usuarios pueden leer, descargar, copiar, distribuir, imprimir, buscar o vincular los textos completos de los artículos, o utilizarlos para cualquier otro fin lícito, sin pedir permiso previo al editor o al autor. Todo lo anterior, de acuerdo con la definición de BOAI de acceso abierto.
Los autores que publican en esta revista están de acuerdo con los siguientes términos: Licencia Creative Commons Atribución-NoComercial permite que el beneficiario de la licencia tenga el derecho de copiar, distribuir, exhibir y representar la obra y hacer obras derivadas para fines no comerciales siempre y cuando reconozca y cite la obra de la forma especificada por el autor o el licenciante. Los autores pueden establecer por separado acuerdos adicionales para la distribución no exclusiva de la versión de la obra publicada en la revista (por ejemplo, situarlo en un repositorio institucional o publicarlo en un libro), con un reconocimiento de su publicación inicial en esta revista. Se permite y se anima a los autores a difundir sus trabajos electrónicamente (por ejemplo, en repositorios institucionales o en su propio sitio web) antes y durante el proceso de envío, ya que puede dar lugar a intercambios productivos, así como a una citación más temprana y mayor de los trabajos publicados (Véase The Effect of Open Access) (en inglés). Lo anterior debe realizarse siempre sobre el artículo ya publicado por Ciencia & Futuro.
Los autores mantienen el control sobre la integridad de sus trabajos y el derecho a ser adecuadamente reconocidos y citados.
A los editores se les otorgan derechos no exclusivos para publicar y distribuir.